UNS S41008 Sheets, SS 410S Plates, AISI SS 410S Stainless Steel 410S Sheets Supplier, Manufacturer and Exporter in India
Din 1.4000 SS 410S Plates, SS UNS S41008 Sheets, Stainless Steel 410S Plates, 410S Stainless Steel Sheets Suppliers in India.
Alloy 410S (UNS S41008) is a low carbon, non–hardening modification of Alloy 410 (UNS S41000) the general purpose 12% chromium martensitic stainless steel. The low carbon and a small alloy addition minimize austenite formation at high temperatures which restricts the alloys ability to harden. 410S remains soft and ductile even when rapidly cooled from above the critical temperature. This non-hardening characteristic helps prevent cracking when the alloy is exposed to high temperatures or welded. 410S is completely ferritic in the annealed condition. It exhibits adequate corrosion resistance similar to 410 and good oxidation resistance.
STAINLESS STEEL 410S SHEETS AND PLATES APPLICATIONS:
- Petroleum Refining and Petrochemical Processing
- Columns
- Distillation trays
- Heat exchangers
- Towers
- Ore Processing
- Mining machinery
- Thermal Processing
- Annealing boxes
- Partitions
- Quenching racks
- Gate valves
- Press plates
STAINLESS STEEL 410S SHEETS AND PLATES OXIDATION RESISTANCE:
- Good oxidation resistance.
- Can be used in continuous service up to 1300°F (705°C).
- Scaling becomes excessive above 1500°F (811°C) in intermittent service.
STAINLESS STEEL 410S SHEETS AND PLATES CORROSION RESISTANCE:
- Corrosion resistance of 410S stainless steel is similar to type 410.
- Resists corrosion in atmospheric conditions, fresh water, mild organic and mineral acids, alkalis and some chemicals.
- Exposure to chlorides in everyday activities (e.g., food preparation, sports activities, etc.) is satisfactory when proper cleaning is performed after exposure to use.
STAINLESS STEEL 410S SHEETS AND PLATES HEAT TREATMENT:
The alloy can not be hardened by heat treatment. It is annealed between 1600 – 1650°F (871 – 899°C), and then air cooled to relieve cold working stresses. 410S should not be exposed to temperatures above 2000°F (1093°C), due to embrittlement. If large grains are found after annealing mildly cold-worked material, the annealing temperature should be decreased to 1200 – 1350°F (649 – 732°C).
STAINLESS STEEL 410S SHEETS AND PLATES WELDING:
410S is generally considered to be weldable by the common fusion and resistance techniques. Special attention should be given to avoid brittle weld fractures during fabrication; this includes minimizing discontinuities, maintaining low weld heat input, and occasionally warming the part somewhat before forming. 410S is generally considered to have slightly poorer weldability than the most common ferritic stainless steel grade 409. A major difference can be attributed to the addition of alloy, to control hardening which results in the need for higher heat input during welding.
STAINLESS STEEL 410S SHEETS AND PLATES CHEMICAL PROPERTIES:
| C | Mn | Si | P | S | Cr | Ni | |
|---|---|---|---|---|---|---|---|
| 410S | 0.08 max | 1.00 max | 1.00 max | 0.04 max | 0.03 max | min: 11.5 max: 14.5 |
0.60 max |
STAINLESSSTAINLESS STEEL 410S SHEETS AND PLATES MECHANICAL PROPERTIES:
| Grade | Tensile Strength ksi (MPa) min | Yield Strength 0.2% offset ksi (MPa) min | Elongation (% in 50mm) min | Hardness (Rockwell B) MAX |
|---|---|---|---|---|
| 410S | 64.4 (444) | 42 (290) | 33 | 75 |
STAINLESSSTAINLESS STEEL 410S SHEETS AND PLATES PHYSICAL PROPERTIES:
| Density lbm/in3 |
Thermal Conductivity (BTU-in/hr- ft. °F) |
Electrical Resistivity (in x 10-6) |
Modulus of Elasticity (psi x 106 |
Coefficient of Thermal Expansion (in/in)/ °F x 10-6 |
Specific Heat (BTU/lb/ °F) |
Melting Range (°F) |
|---|---|---|---|---|---|---|
| at 68°F: 0.280 | 187 at 212°F | 23.7 at 68°F | 29 | 6.0 at 32 – 212°F | 0.11 at 68°F to 212°F | 2700 to 2790 |
| 7.5 at 68 – 1200°F |
Harsh steel Supplies and Exports Stainless steel 410S Strips from 2.5mm wide to 400mm, slit to close tolerances. We supply in below specifications:-
| STAINLESS STEEL PLATES,GRADES WITH THICKNESS AND WIDTH | |
|---|---|
| Thickness Range of Stainless Plate | 3/16″ Thru 6″ Thick Stainless Steel Plate |
| Common Widths of Stainless Plate Coil | 48″ Wide – 60″ Wide – 72″ Wide – 78.75″ (2 Meter) wide – 84″ wide – 96″ wide – 120″ wide & other widths upon customer request. |
| 200-300 Series Stainless Steel Grades | 202- 301 – 304 – 304L – 304L Polished – 304H – 309 – 309S – 309H – 310 – 310S – 310H – 316L – 316L Polished – 317L – 317LMN – 321 – 321H – 330 – 347 347H |
| 400 Series Stainless Steel Grades | 405 – 410 – 410S – 416 – 420 – 440C |
| Duplex Stainless Steel Grades | LDX 2101 – Duplex 2205 – Duplex 2507 |
| Precipitation Hardening Grades | 17-4PH – 17-4 H1150 (per customer request) – 15-5PH |
| Nickel Alloy Grades | Alloy 20 – Alloy 200 – Alloy 400 – Alloy 600 – Alloy 800 – Alloy 800HT – Alloy C-276 (nickel grades may require lead time) |
We export our STAINLESS STEEL 410S SHEETS AND PLATES products to Western and Eastern Europe, Saudi Arabia, Bangladesh, United States, United Arab Emirates, Canada, Angola, Argentina, Austria, Azerbaijan, Pakistan, Peru, Chile, Spain, France, United Kingdom, Indonesia, Israel, Iran, Kuwait, Mexico, Malaysia, Nigeria, Serbia, Singapore, Taiwan, Chile, Venezuela, Ecuador, Netherlands, Brazil, Colombia, Ghana, Iran, Denmark, Poland, Australia, Afghanistan, Bahrain, Costa Rica, Egypt, Iraq, Jordan, South Korea, Kazakhstan, Sri Lanka, Lithuania, Norway, Oman, Philippines, Poland, Qatar, Russia, Vietnam, South Africa, Nigeria, Mexico, Turkey, Hungary, Algeria, Belarus, Belgium, Bhutan, Bolivia, Bulgaria, Croatia, Czech Republic, Estonia, Finland, Greece, Italy, Japan, Libya, Romania, Thailand, Trinidad & Tobago,Tunisia, Ukraine, Yemen, Hong Kong, Gabon, China, Portugal, Switzerland, New Zealand, Sweden, Slovakia, Kenya, Lebanon, Morocco, Mongolia etc. We are sure that we also can cover the requirements requested by your company you can email us at harshsteel@ymail.com for your instant requirements.