Stainless Steel 309S Angle, UNS S30908 Angle Supplier & Exporter

STAINLESS STEEL 309S ANGLE GENERAL PROPERTIES:

Alloys 309 and 309S are austenitic chromium-nickel stainless steels that are often used for higher temperature applications. Due to their high chromium and nickel content, Alloys 309 and 309S are highly corrosion resistant, have outstanding resistance to oxidation, and excellent heat resistance while providing good strength at room and elevated temperatures. The only significant difference between 309 and 309S is the carbon content. Alloy 309S has a much less carbon composition which minimizes carbide precipitation and improves weldability.

STAINLESS STEEL 309S ANGLE APPLICATIONS:

Alloys 309 and 309S are used exclusively for their high temperature oxidation resistance, excellent high temperature strength, along with their resistance to creep deformation and environmental attack. Some examples include, but are not limited to:

• Heating elements
• Aircraft and jet engine parts
• Heat exchangers
• Carburizing annealing products
• Sulfite liquor handling equipment
• Kiln liners
• Boiler baffles
• Refinery and chemical processing equipment
• Auto exhaust parts

STAINLESS STEEL 309S ANGLE CORROSION RESISTANCE:

• Provide excellent corrosion resistance
• More resistant to marine atmospheres than Alloy 304
• Often used at higher temperatures to take advantage of their oxidation resistance
• Have high resistance to sulfite liquors
• Generally considered heat resistant alloys
• Destructive scaling temperature is approximately 2000oF
• Good scaling resistance with regard to continuous and intermittent services

STAINLESS STEEL 309S ANGLE HIGH TEMPERATURECORROSION:

Alloy 309 resists high temperature corrosion in most in-service conditions. Operating temperatures are as follows:

• Oxidizing conditions (max. sulfur content–2 g/m3)
  • 1922°F (1050°C) continuous service
  • 2012°F (1100°C) peak temperature
• Oxidizing conditions (max. sulfur greater than 2 g/m3)
  • 1742°F (950°C) maximum temperature
• Low oxygen atmosphere (max. sulfur content–2 g/m3)
  • 1832°F (1000°C) maximum temperature
• Nitriding or carburizing atmospheres
  • 1562–1742°F (850–950°C) maximum

The alloy does not perform as well as Alloy 600 (UNS N06600) or Alloy 800 (UNS N08800) in reducing, nitriding or carburizing atmospheres, but it does outperform most heat resistant stainless steels in these conditions.

STAINLESS STEEL 309S ANGLE FABRICATION:

• Can be roll formed, stamped, and drawn readily
• In process annealing is often required to reduce hardness and increase ductility

STAINLESS STEEL 309S ANGLE HEAT RESISTANCE:

• Cannot be hardened through heat treatment because the consist solely of austenite at room temperature
• Higher tensile and yield strengths that can be obtained through cold working and not followed by full annealing are not stable at the higher temperatures where these alloys are used
• Creep properties can be negatively affected by the use of cold worked material at these higher temperatures

STAINLESS STEEL 309S ANGLE WELDING CHARACTERISTICS:

• The austenitic class of stainless steels is generally considered to be weldable
• Generally considered to have weldability equivalent to the most common alloys of the austenitic class 304 and 304L
• Special consideration is needed to compensate for a higher coefficient of thermal expansion to avoid warping and distortion

STAINLESS STEEL 309S ANGLE CHEMICAL PROPERTIES:

	C	Mn	Si	P	S	Cr	Ni	Fe
309	max: 0.20	2.0 max	0.75 max	0.045 max	0.03 max	min: 22.0 max: 24.0	min: 12.0 max: 15.0	Balance
309H	min: 0.04 max: 0.10	2.0 max	0.75 max	0.045 max	0.03 max	min: 22.0 max: 24.0	min: 12.0 max: 15.0	Balance

STAINLESS STEEL 309S ANGLE MECHANICAL PROPERTIES:

Grade	Tensile Strength ksi (min)	Yield Strength 0.2% ksi (min)	Elongation %	Hardness (Brinell) MAX
309/H	40	30	40	217

STAINLESS STEEL 309S ANGLE PHYSICAL PROPERTIES:

Density lbm/in3	Thermal Conductivity (BTU/h ft. °F)	Electrical Resistivity (in x 10-6)	Modulus of Elasticity (psi x 106	Coefficient of Thermal Expansion (in/in)/ °F x 10-6	Specific Heat (BTU/lb/ °F)	Melting Range (°F)
at 68°F: 0.285	9.0 at 32- 212°F	30.7 at 68°F	28.5	8.28 at 32 – 212°F	0.1200 at 68°F to 212°F	2500-2590

WHY TO CHOOSE HARSH STEEL STAINLESS STEEL ANGLE BARS?

• Corrosion resistance
• Durable
• Very sturdy
• Easy to install
• Fire and heat resistance
• Rust free
• Abrasion free

HARSH STEEL STAINLESS STEEL ANGLE BARS USED IN?

• Architectural applications
• Bridges
• Transmission towers
• Hoisting and conveying machinery
• Ships
• Industrial furnace
• Reaction tower
• Container frame and warehouse shelves
• Multi-storied building
• Fabrication

STAINLESS STEEL 309S ANGLE DETAILS:

• Finish:Hot Rolled Annealed & Pickled (HRAP)
• Length: 3 to 7 Meters / 12 to 24 feet
• End Finish: Both ends are marked with special colors
• Size tolerance : ASTM A276/484 / DIN 1028
• Packing: Bars are packed in 500 to 1,000 kgs bundles in waterproof HDPE cloth Standard Export Seaworthy.
• Delivery: Within 60-70 Days from the order finalization
• Grades : AISI 201, 202, 204cu, 304, 304L, 316, 410, 420, 430

STAINLESS STEEL 309S ANGLE SIZES:

Width (mm)	Thickness (mm)	Width (Inches)	Thickness (Inches)
20 x 20	3 to 5	3/4"	1/8 to 1/4
25 x 25	3 to 5	1"	1/8 to 1/4
30 x 30	3 to 5	1.1/8	1/8 to 1/4
32 x 32	3 to 6	1.1/4	1/8 to 1/4
35 x 35	3 to 6	1.3/8	1/8 to 1/4
38 x 38	3 to 6	1.1/2	1/8 to 1/4
40 x 40	3 to 6	1.5/8	1/8 to 1/4
45 x 45	3 to 6	1.3/4	1/8 to 1/4
50 x 50	3 to 6	2"	1/8 to 1/4
60 x 60	5 to 6	2.3/8	3/16 to 1/4
65 x 65	5 to 6	2.1/2	3/16 to 1/4
70 x 70	5 to 6	2.3/4	3/16 to 1/4
75 x 75	5 to 6	3"	3/16 to 1/4

---